Zingwe za Nayiloni Zotentha Zogwiritsidwa Ntchito mu Windows
Mawonekedwe I, mawonekedwe C, mawonekedwe T, mawonekedwe a CT ndi mawonekedwe a HK ndi mawonekedwe ambiri, tithanso malinga ndi zomwe makasitomala amafuna kapena zojambula kuti tisinthe mawonekedwe ena apadera.
1.Effectively kuchuluka matenthedwe mu dongosolo katundu kutchinjiriza.
2.Reduces condensation pa zenera.
3.Sound insulated.
4.Kupititsa patsogolo chitonthozo ndi chikhalidwe cha moyo.
5.Possible double color zokutira zimapereka zotsatira zabwino zokongoletsa.
6.Mawonekedwe osiyanasiyana adzapangidwira zofuna za kasitomala.
7.Kutentha kogwira ntchito kwa mzere wotsekemera wa kutentha ndi 220 ° C, Melting Point kufika ku 246 ° C.Izi zimathandiza kuti ❖ kuyanika pambuyo pa kusonkhanitsa mbiri yamagulu.
8.Kukana kwa dzimbiri, kukana nyengo, kukana kutentha, kukana kwa alkali komanso moyo wautali wogwiritsidwa ntchito.
9.linear dilation coefficient pafupifupi yofanana ndi mbiri ya aluminiyamu.
AYI. | Kanthu | Chigawo | GB/T 23615.1-2009 | HC-Technical specifications |
| Zinthu Zakuthupi | |||
1 | Kuchulukana | g/cm3 | 1.3±0.05 | 1.28-1.35 |
2 | Linear kukulitsa koyefithi | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
3 | Vicat kufewetsa kutentha | ºC | ≥230ºC | ≥233ºC |
4 | Malo osungunuka (0.45MPa) | ºC | ≥240ºC | ≥240 |
5 | Kuyesa ming'alu yokhazikika | - | Palibe ming'alu | Palibe ming'alu |
6 | Kuuma kwa nyanja | - | 80 ±5 | 80-85 |
7 | Mphamvu zamphamvu (zosasankhidwa) | KJ/m2 | ≥35 | ≥38 |
8 | Mphamvu yamphamvu (longitudinal) | MPa | ≥80a | ≥82a |
9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
10 | Elongation panthawi yopuma | % | ≥2.5 | ≥2.6 |
11 | Mphamvu yamphamvu (yodutsa) | MPa | ≥70a | ≥70a |
12 | Kutentha kwakukulu kwamphamvu (kudutsa) | MPa | ≥45a | ≥47a |
13 | Kutentha kwapang'onopang'ono mphamvu (zopingasa) | MPa | ≥80a | ≥81a |
14 | Mphamvu yolimbana ndi madzi (transverse) | MPa | ≥35a | ≥35a |
15 | Kulimbana ndi ukalamba mphamvu yolimba (yodutsa) | MPa | ≥50a | ≥50a |
1.Zitsanzo za madzi ocheperapo 0.2% polemera.
2.Nyengo za labotale:(23±2)ºC ndi (50±10)% chinyezi chachibale.
3.Mafotokozedwe olembedwa ndi "a" amangogwira ntchito ku mzere wa I-mawonekedwe apo ayi, zomwe zatsirizidwa pakati pa wogulitsa ndi wogula kudzera muzokambirana, zidzalembedwa mu mgwirizano kapena kugula.
Zingwezo zidzasungidwa m'malo opumira komanso owuma, oyikidwa mozungulira, kutchera khutu ku madzi, kusunga kutali ndi gwero la kutentha, kupewa kupanikizika kwakukulu ndi kukhudzana ndi asidi, alkali komanso zosungunulira za organic.
Tili ndi mphamvu zopanga 100000 metres patsiku.Pazidziwitso wamba, tili ndi nkhungu, ndipo tidzatumizidwa mu masiku 15-20 ogwira ntchito atalandira gawolo.